dc.description.abstractLight emitting Al-Tb/SiO2 nanomultilayers (NMLs) for optoelectronic applications have been produced and characterized. The active layers were deposited by electron beam evaporation onto crystalline silicon substrates, by alternatively evaporating nanometric layers of Al, Tb, and SiO2. After deposition, all samples were submitted to an annealing treatment for 1 h in N2 atmosphere at different temperatures, ranging from 700 to 1100 °C. Transmission electron microscopy confirmed the NML structure quality, and by complementing the measurements with electron energy-loss spectroscopy, the chemical composition of the multilayers was determined at the nanoscopic level. The average composition was also measured by X-ray photoelectron spectroscopy (XPS), revealing that samples containing Al are highly oxidized. Photoluminescence experiments exhibit narrow emission lines ascribed to Tb3+ ions in all samples (both as-deposited and annealed ones), together with a broadband related to SiO2 defects. The Tb-related emission intensity in the sample annealed at 1100 °C is more than one order of magnitude higher than identical samples without Al. These effects have been ascribed to the higher matrix quality, less SiO2 defects emitting, and a better Tb3+ configuration in the SiO2 matrix thanks to the higher oxygen content favored by the incorporation of Al atoms, as revealed by XPS experiments.-
dc.format.extent8 p.-
dc.publisherAmerican Institute of Physics-
dc.relation.isformatofReproducció del document publicat a:
dc.relation.ispartofJournal of Applied Physics, 2016, vol. 120, p. 135302-135302-
dc.rights(c) American Institute of Physics , 2016-
dc.subject.classificationPropietats òptiques-
dc.subject.classificationFeixos electrònics-
dc.subject.otherOptical properties-
dc.subject.otherElectron beams-
dc.titleStructural and optical properties of Al-Tb/SiO2 multilayers fabricated by electron beam evaporation-
Appears in Collections:Articles publicats en revistes (Enginyeria Electrònica i Biomèdica)

Files in This Item:
File Description SizeFormat 
664431.pdf1.86 MBAdobe PDFView/Open

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.