Giró Paloma, JessicaAl-Shannaq, RefatFernández Renna, Ana InésFarid, Mohammed M.2016-11-172016-11-172015-12-261996-1944https://hdl.handle.net/2445/103782A method for preparing and characterizing microencapsulated phase change materials (MPCM) was developed. A comparison with a commercial MPCM is also presented. Both MPCM contained paraffin wax as PCM with acrylic shell. The melting temperature of the PCM was around 21 C, suitable for building applications. The M-2 (our laboratory made sample) and Micronalr DS 5008 X (BASF) samples were characterized using SEM, DSC, nano-indentation technique, and Gas Chromatography/Mass spectrometry (GC-MS). Both samples presented a 6 m average size and a spherical shape. Thermal energy storage (TES) capacities were 111.73 J g 1 and 99.3 J g 1 for M-2 and Micronalr DS 5008 X, respectively. Mechanical characterization of the samples was performed by nano-indentation technique in order to determine the elastic modulus (E), load at maximum displacement (Pm), and displacement at maximum load (hm), concluding that M-2 presented slightly better mechanical properties. Finally, an important parameter for considering use in buildings is the release of volatile organic compounds (VOC's). This characteristic was studied at 65 C by CG-MS. Both samples showed VOC's emission after 10 min of heating, however peaks intensity of VOC's generated from M-2 microcapsules showed a lower concentration than Micronalr DS 5008 X.13 p.application/pdfengcc-by (c) Giró Paloma, Jessica et al., 2015http://creativecommons.org/licenses/by/3.0/esCompostos orgànics volàtilsCalorimetriaMicroencapsulacióVolatile organic compoundsCalorimetryMicroencapsulationinfo:eu-repo/semantics/article6564092016-11-17info:eu-repo/semantics/openAccess28787812