Screen printed La2/3Sr1/3MnO3 thick films on alumina substrates

Abstract

We report here on the preparation of La2/3Sr1/3MnO3 magnetoresistive thick films on polycrystalline Al2O3 substrates by using the screen printing technique. It is shown that films can be obtained using high temperature sintering. While there is a reacted layer, this improves adhesion and is not too troublesome if the films are made thick enough. It is shown that PbO-B2O3-SiO2 glass additives allow sintering at lower temperatures and can be used to improve the mechanical stress of the films. However, it is found that glass concentrations large enough to significantly improve the film adherence result in a weak low field magnetoresistance probably because grains are coated with high resistivity material. Strategies to overcome these difficulties are discussed.