The effect of anode support on the electrochemical performance of microtubular solid oxide fuel cells fabricated by gel-casting
Títol de la revista
Director/Tutor
ISSN de la revista
Títol del volum
Recurs relacionat
Resum
Different cell configurations of anode-supported microtubular solid oxide fuel cells (mT-SOFCs) using samaria-doped ceria (SDC) as the electrolyte were fabricated. Several cells were processed varying the porosity and wall thickness (outer diameter) of NiO
SDC tubular supports. Suitable aqueous slurry formulations of NiO
SDC for gel-casting were prepared using agarose, as a gelling agent, and sucrose, as a pore former. The subsequent NiO
SDC anode functional layer (AFL), the SDC electrolyte and the La0.6Sr0.4Co0.2Fe0.8O3-d
SDC cathode were deposited by spray-coating. Pre-sintering temperatures of the supports were optimized from linear shrinkage curves, thus obtaining after co-sintering, a dense electrolyte without anode-electrolyte delamination. Electrochemical characterization of mT-SOFC cells fabricated by agarose gel-casting is reported by the first time. The cell with a support of 2.6 mm diameter, 380 mm wall thickness, an active area of 1 cm2 and added porosity, using 10 wt% sucrose, achieved a maximum power density of about 400 mW cm2 at 650 ºC.
SDC tubular supports. Suitable aqueous slurry formulations of NiO
SDC for gel-casting were prepared using agarose, as a gelling agent, and sucrose, as a pore former. The subsequent NiO
SDC anode functional layer (AFL), the SDC electrolyte and the La0.6Sr0.4Co0.2Fe0.8O3-d
SDC cathode were deposited by spray-coating. Pre-sintering temperatures of the supports were optimized from linear shrinkage curves, thus obtaining after co-sintering, a dense electrolyte without anode-electrolyte delamination. Electrochemical characterization of mT-SOFC cells fabricated by agarose gel-casting is reported by the first time. The cell with a support of 2.6 mm diameter, 380 mm wall thickness, an active area of 1 cm2 and added porosity, using 10 wt% sucrose, achieved a maximum power density of about 400 mW cm2 at 650 ºC.
Matèries (anglès)
Citació
Citació
MORALES COMAS, Miguel, LAGUNA BERCERO, Miguel a., NAVARRO, M. elena, ESPIELL ÁLVAREZ, Ferran, SEGARRA RUBÍ, Mercè. The effect of anode support on the electrochemical performance of microtubular solid oxide fuel cells fabricated by gel-casting. _RSC Advances_. 2015. Vol. 5, núm. 49, pàgs. 39350-39357. [consulta: 28 de gener de 2026]. ISSN: 2046-2069. [Disponible a: https://hdl.handle.net/2445/128161]