Nanocrystalline M-type hexaferrite powders: preparation, geometric and magnetic propertiess
Títol de la revista
Director/Tutor
ISSN de la revista
Títol del volum
Recurs relacionat
Resum
Co-Ti-Sn-Ge substituted M-type bariumhexaferrite powders with mean grain sizes between about 10 nm and about 1 ¿m and a narrow size distribution were prepared reproducibly by means of a modified glass crystallization method. At annealing temperatures between 560 and 580°C of the amorphous flakes nanocrystalline particles grow. They behave superparamagnetically at room temperature and change into stable magnetic single domains at lower temperatures. The magnetic volume of the powders is considerably less than the geometric one. However, the effective anisotropy fields are larger by a Factor of two to three.
Matèries (anglès)
Citació
Citació
GORNERT, P., PFEIFFER, H., SINN, E., MULLER, Rainer, SCHUPPEL, W., ROSLER, M., BATLLE GELABERT, Xavier, GARCÍA DEL MURO Y SOLANS, Montserrat, TEJADA PALACIOS, Javier, GALÍ MEDINA, Salvador. Nanocrystalline M-type hexaferrite powders: preparation, geometric and magnetic propertiess. _IEEE Transactions on Magnetics_. 1994. Vol. 30, núm. 2 (Part 1-2), pàgs. 714-716. [consulta: 29 de gener de 2026]. ISSN: 0018-9464. [Disponible a: https://hdl.handle.net/2445/8582]