Glass-ceramic crystallization from tailings of the Morille tungsten deposit, Spain
Títol de la revista
Director/Tutor
ISSN de la revista
Títol del volum
Recurs relacionat
Resum
The potential of the tailings from the Morille scheelite-bearing calc-silicate deposit as a commercial raw material for inert glass-ceramic was determined. Nucleation and crystal growth temperatures of glass were studied. The temperatures of maximum nucleation rate of the parent glass are 612 °C and 660 °C and crystal growth is at 776 °C and 1047 °C. At 776 °C a glass-ceramic of nepheline, wollastonite and akermanite is formed. In glasses treated at higher temperature nepheline becomes unstable and at 1047 °C a wollastonite-akermanite glass ceramic was obtained. The leaching tests show that the potentially toxic elements are effectively bound in the structure of the glass-ceramic, which can be considered inert.
Matèries
Matèries (anglès)
Citació
Citació
ALFONSO ABELLA, María pura, TOMASA, Oriol, GARCIA VALLÈS, Maite, TARRAGÓ AYMERICH, Mariona, MARTÍNEZ MANENT, Salvador. Glass-ceramic crystallization from tailings of the Morille tungsten deposit, Spain. _Materials Letters_. 2022. Vol. 312, núm. 131694. [consulta: 23 de gener de 2026]. ISSN: 0167-577X. [Disponible a: https://hdl.handle.net/2445/191680]